Structures by: Yamanaka T.
Total: 129
Clinopyroxene
FeGeO3
American Mineralogist (2000) 85, 1485-1491
a=9.798Å b=9.140Å c=5.205Å
α=90° β=101.80° γ=90°
Clinopyroxene
FeGeO3
American Mineralogist (2000) 85, 1485-1491
a=9.746Å b=9.084Å c=5.177Å
α=90° β=101.52° γ=90°
Clinopyroxene
FeGeO3
American Mineralogist (2000) 85, 1485-1491
a=9.651Å b=8.988Å c=5.136Å
α=90° β=100.97° γ=90°
Clinopyroxene
FeGeO3
American Mineralogist (2000) 85, 1485-1491
a=9.600Å b=8.912Å c=5.108Å
α=90° β=100.67° γ=90°
Clinopyroxene
FeGeO3
American Mineralogist (2000) 85, 1485-1491
a=9.287Å b=8.400Å c=4.850Å
α=90° β=100.025° γ=90°
GeMgO3
GeMgO3
American Mineralogist (2005) 90, 1301-1307
a=4.9375Å b=4.9375Å c=13.743Å
α=90° β=90° γ=120°
MgO3Ti
MgO3Ti
American Mineralogist (2005) 90, 1301-1307
a=5.0540Å b=5.0540Å c=13.898Å
α=90° β=90° γ=120°
Perovskite
CaO3Ti
American Mineralogist (2002) 87, 1183-1189
a=5.4043Å b=5.4224Å c=7.6510Å
α=90° β=90° γ=90°
Perovskite
Ca0.75O3Sr0.25Ti
American Mineralogist (2002) 87, 1183-1189
a=5.4440Å b=5.4591Å c=7.7213Å
α=90° β=90° γ=90°
Tausonite
Ca0.4O3Sr0.6Ti
American Mineralogist (2002) 87, 1183-1189
a=5.4784Å b=5.4791Å c=7.7517Å
α=90° β=90° γ=90°
Tausonite
Ca0.35O3Sr0.65Ti
American Mineralogist (2002) 87, 1183-1189
a=5.4801Å b=5.4801Å c=7.7619Å
α=90° β=90° γ=90°
Tausonite
O3SrTi
American Mineralogist (2002) 87, 1183-1189
a=5.5202Å b=5.5202Å c=7.8067Å
α=90° β=90° γ=90°
Tausonite
Ca0.35O3Sr0.65Ti
American Mineralogist (2002) 87, 1183-1189
a=5.423Å b=5.420Å c=7.647Å
α=90° β=90° γ=90°
Tausonite
Ca0.35O3Sr0.65Ti
American Mineralogist (2002) 87, 1183-1189
a=5.415Å b=5.412Å c=7.637Å
α=90° β=90° γ=90°
Magnesium dialuminium oxide
Al2MgO4
Kobutsugaku Zasshi (= Journal of the Mineralogical Society of Japan) (1983) 16, 221-231
a=8.2065(12)Å b=8.2065(12)Å c=8.2065(12)Å
α=90° β=90° γ=90°